Filament Data

Product	Key Feature	Print Temp.	Density	Tensile Strength	Elongation	Impact	Vicat Softening	Melting / MFI
PLA PRO (+)	Low-viscosity, easy-support removal	190–220 °C	1.21–1.30 g/cm³	17–18 MPa Printed ≥30 MPa	4.6–5.3%	1–3 kJ/m²	61.5 °C	178.5 °C
PLA Silk	PLA Shiny Silk Finish	210–230 °C	1.21–1.30 g/cm³	17–18 MPa Printed ≥28 MPa	4.6–5.3%	1–3 kJ/m²	61.5 °C	168.5 °C
PLA Matte	PLA Matte Finish	190–220 °C	1.21–1.30 g/cm³	11–12 MPa Printed ≥23 MPa	4.6–5.3%	1–3 kJ/m²	61.5 °C	178.5 °C
PLA Marble	Marble Filament	190–220 °C	1.21–1.30 g/cm³	17–18 MPa Printed ≥30 MPa	4.6–5.3%	1–3 kJ/m²	61.5 °C	178 °C
PLA Wood	10-15% Bamboo powder, nature color and white color. Realistic Wood texture.	180–200 °C	1.02 g/cm³	Printed 25-28 MPa	at Break 14%	----	61.5 °C	168 °C
PLA Pro Rainbow	Fast Colour Change, 1-3meters	190–220 °C	1.21–1.30 g/cm³	17–18 MPa Printed ≥30 MPa	4.6–5.3%	1–3 kJ/m²	61.5 °C	178.5 °C
PLA Gradients	Gradient Colour Changes	190–220 °C	1.21–1.30 g/cm³	17–18 MPa Printed ≥30 MPa	4.6–5.3%	1–3 kJ/m²	61.5 °C	178.5 °C
PLA Luminous	Absorbs UV Light, Glows in the dark	190–220 °C	1.21–1.30 g/cm³	17–18 MPa Printed ≥30 MPa	4.6–5.3%	1–3 kJ/m²	61.5 °C	178.5 °C

Product	Key Feature	Print Temp.	Density	Tensile Strength	Elongation	Flexural	Impact	Vicat	HDT	Bed Temp.
PETG Pro	High transparency, chemical resistance	220–240 °C	1.27 g/cm³	Yield 53 MPa Break 26 MPa	70%	Strength 80 MPa Modulus 2150 MPa	90 J/m	83 °C	74 °C	0–40 °C
PETG Hyper	High-flow PETG for speed	210–230 °C	1.27 g/cm³	Break 45–50 MPa	7%	Strength 55–60 MPa Modulus 2150 MPa	—	83 °C	74 °C	0–40 °C
PETG-CRCF	Coated carbon fiber (15–20% content, 0.1–0.5mm fibers)	250–280 °C	1.29 g/cm³	3D-print 65 MPa	≤8%	—	—	—	78–82 °C	≥90 °C

Product	Key Feature	Print Temp.	Density	Tensile Strength	Elongation	Bending / Modulus	Impact	Tg	HDT
ABS Pro	Low-warp, glossy, high toughness	230–250 °C	1.057 g/cm³	Break 33.2 MPa Rate 2.9%	—	Bending stress 66.9 MPa Modulus 2260 MPa	Notched Impact P16	106.7 °C	106 °C
ABS Hyper	High-flow ABS, low warpage	230–250 °C	1.07 g/cm³	Break 33.2 MPa Rate 2.9%	—	Bending stress 50–60 MPa Modulus 2200 MPa	Notched Impact P16	106.7 °C	106 °C
ABS-CRCF	Coated carbon fiber ABS (15–25% CF, 0.1–3mm fibers)	240–280 °C	1.05 g/cm³ CF 15–25% Fiber 0.1–3 mm	3D-print 65 MPa	≤8%	—	—	—	78–88 °C

Product	Key Feature	Print Temp.	Density	Tensile Strength	Elongation	Flexural Strength	Flexural Modulus	Impact	Vicat	HDT
ASA Pro	Excellent UV resistance, outdoor durability, glossy surface	240–260 °C	1.07 g/cm³	31 MPa (3D Print) 47 MPa (Injection)	1.8–2.2% (3D Print) 20% (Injection)	44–47 MPa (3D Print) 65 MPa (Injection)	1680 MPa (3D Print) 2100 MPa (Injection)	18 kJ/m² (Charpy) 18 kJ/m² (Izod)	196 °C	80 °C